  • Tool Steel 
    • Cold Work Steel
      Chemical composition C = 2.0, Si = 0.25, Mn = 0.30, Cr = 11.5
      Supply Condition Annealed 250 HB
      Nearest Equivalent DIN 1.2080, AISI D3, JIS SKD1
      Chemical composition C = 1.6, Cr = 11.5, Mo = 0.6, V = 0.3, W = 0.5
      Supply Condition Annealed 250 HB
      Nearest Equivalent DIN 1.2601 , AISI D2, JIS SKD11
      Chemical composition C = 2.1, Si = 0.25, Mn = 0.35, Cr = 11.5, W = 0.7
      Supply Condition Annealed 250 HB
      Nearest Equivalent DIN 1.2436, AISI D6
      Chemical composition C = 1.55, Si = 0.25, Mn = 0.35, Cr = 11.8, Mo = 0.8, V = 0.95
      Supply Condition Annealed 235 - 250 HB
      Nearest Equivalent DIN 1.2379, AISI D2, JIS SKD 11
      Chemical composition C = 1.10, Si = 0.90, Mn = 0.40, Cr = 8.30, Mo = 2.10,V = 0.50,+ Al, Nb
      Supply Condition Annealed 250 HB
      Chemical composition C = 0.82, Si = 0.70, Mn = 0.40, Cr = 8.00, Mo = 1.60, V = 0.60+ Al = +
      Supply Condition Annealed 240 HB Max.
      Chemical composition C = 2.47, Si = 0.55, Mn = 0.40, Cr = 4.20, Mo = 3.8, V = 9.00,W = 1.00, Co = 2.00
      Supply Condition Annealed 280 HB Max.
      Chemical composition C = 1.40, Cr = 6.40, Mo = 1.50, V = 3.70, W = 350, Nb = +
      Supply Condition Annealed 280 HB Max.
      Chemical composition C = 0.95, Si = 0.25, Mn = 1.10, Cr = 0.55, V = 0.10, W = 0.55
      Supply Condition Annealed 225 HB
      Nearest Equivalent DIN 1.2510, AISI O1, JIS SKS21 (SKS3)
      Chemical composition C = 1.18, Si = 0.25, Mn = 0.30, Cr = 0.70, V = 0.10
      Supply Condition Annealed 220 HB
      Nearest Equivalent DIN 1.2210, 115CrV3
    • Hot Work Steel
      Chemical composition C = 0.39, Cr = 5.2, Mo = 1.4, V = 0.95, Si = 1.1, Mn = 0.40
      Supply Condition Annealed 230 – 235 HB
      Nearest Equivalent DIN 1.2344, AISI H13, JIS SKD61
      Chemical composition C = 0.38, Si = 0.4, Mn = 0.4, Cr = 5.0, Mo = 2.8, V = 0.65
      Supply Condition Annealed 230 – 235 HB
      Nearest Equivalent DIN 1.2367
      Chemical composition C = 0.39, Cr = 2.9, Mn = 0.35, Mo = 2.8, V = 0.65, Si = 0.3,Co = 2.9
      Supply Condition Annealed 230 - 235 HB
      Nearest Equivalent DIN 1.2885, ~X32CrMoCoV3-3-3
      Chemical composition C = 0.50, Cr = 4.50, Mo = 3.00, V = 0.55, Si = 0.20, Mn = 0.25
      Supply Condition Annealed max 205 HB
      Chemical composition C = 0.38, Cr = 5.00, Mo = 2.80, V = 0.65, Si = 0.20, Mn = 0.25
      Supply Condition Annealed max 205 HB
      Nearest Equivalent DIN ~1.2367
      Chemical composition C = 0.55, Si = 0.25, Mn = 0.75, Cr = 1.1, Mo = 0.50, Ni = 1.7,V = 0.10
      Supply Condition Prehardened 38-42 HRC
      Nearest Equivalent DIN 1.2714, AISI L6, JIS SKT4
    • Plastic Mould Steel
      Chemical composition C = 0.40, Si = 0.3, Mn = 1.5, Cr = 2.0, Mo = 0.2, S = 0.02,Ni = 1.0
      Supply Condition Prehardened 28–32 HRC (280–325 HB), High Hard 38–42 HRC
      Nearest Equivalent DIN 1.2738, ASSAB 718
      Chemical composition C = 0.35-0.45, Si = 0.20-0.40, Mn = 1.30-1.60, Cr = 1.80-2.10,Mo = 0.15-0.25, S = 0.002 max
      Supply Condition Prehardened 28-32 HRC (280-325 HB)
      Nearest Equivalent AISI P20, DIN 1.2311
      Chemical composition C = 0.40, Si = 0.40, Mn = 1.50, Cr = 1.90, Mo = 0.20, S = 0.07
      Supply Condition Prehardened 28-32 HRC (280-325 HB)
      Nearest Equivalent DIN 1.2312, AISI P20
      Chemical composition C = 0.38, Si = 0.30, Mn = 1.50, Cr = 2.00, Mo = 0.20, Ni = 1.10
      Supply Condition Harden and tempered 38-42 HRC (350-400 HB), High Hard
      Nearest Equivalent DIN 1.2738
      Chemical composition C = 0.38, Si = 0.4, Cr = 16.0, Mo = 1.0, Ni = 0.8, Mn = 0.65
      Supply Condition Prehardened 28-32 HRC
      Nearest Equivalent DIN 1.2316, ~X36CrMo17
      Chemical composition C = 0.27, Cr = 14.7, Mo = 1.00, Ni = 0.80, Si = 0.30, Mn = 0.55,+ N
      Supply Condition Prehardened 28-32 HRC, High Hard 38-42 HRC
      Nearest Equivalent DIN ~1.2316
      Chemical composition C = 0.41, Si = 0.70, Mn = 0.45, Cr = 14.30,Mo = 0.60, V = 0.20
      Supply Condition Annealed 200 HB
      Nearest Equivalent DIN 1.2083, AISI 420, JIS SUS 420J2, ASSAB STAVAX
      Chemical composition C = 0.05, Si = 0.20, Mn = 0.90, S = 0.12, Cr = 12.80, Ni = +
      Supply Condition Prehardened 28-32 HRC (280-320 HB)
      Chemical composition C = 0.28, Si = 0.3, Mn = 0.3, Cr = 13.5, +N
      Supply Condition Annealed 220 HB
      Chemical composition C = 0.54, Si = 0.45, Mn = 0.40, Cr = 17.30, Mo = 1.10, V = 0.10,+ N
      Supply Condition Annealed 260 HB
      Chemical composition C = 0.13, Si = 0.30, Mn = 2.00, Cr = 0.35, Ni = 3.50, Cu = 1.20,Al = 1.20
      Supply Condition Hardened 38-42 HRC
      Nearest Equivalent AISI ~P21, DAIDO NAK80
    • Powder Metallurgical
      S790 PM
      S290 PM
      S390 PM
      S590 PM
  • High Speed Steel
    Chemical composition C = 0.90, Cr = 4.1, Mo = 5.0, V = 1.8, W = 6.2
    Supply Condition Annealed 280 HB Max.
    Nearest Equivalent DIN 1.3343, AISI M2, JIS SKH51
    Chemical composition C = 0.92, Si = 0.4, Mn = 0.3, Cr = 4.1, Mo = 5.0, V = 1.9,W = 6.4, Co = 4.8
    Supply Condition Annealed 270-300 HB
    Nearest Equivalent DIN 1.3243, AISI M41, JIS SKH55
    Chemical composition C = 1.30, Si = 0.60, Mn 0.30, Cr = 4.20, Mo = 5.00, V = 3.00,W = 6.30
    Supply Condition Annealed 280 HBx
    Nearest Equivalent DIN 1.3345, ASSAB ASP23
    Chemical composition C = 2.00, Si = 0.5, Mn = 0.3, Cr = 3.8, Mo = 2.5, V = 5.1,W = 14.3, Co = 11.0
    Supply Condition Annealed 350 HB Max
    Chemical composition C = 1.64, Si = 0.60, Mn = 0.30, Cr = 4.80, Mo = 2.00,V = 4.80, W = 10.40, Co = 8.00
    Supply Condition Annealed 300 HB Max
    Nearest Equivalent ASSAB ASP60
    Chemical composition C = 1.1, Si = 0.5, Mn = 0.2, Cr = 3.9, Mo = 9.2, V = 1.0,W = 1.4, Co = 7.8
    Supply Condition Annealed 280 HB Max
    Nearest Equivalent DIN 1.3247, AISI M42, JIS ~SKH59
    Chemical composition C = 1.29, Si = 0.60, Mn = 0.30, Cr = 4.20, Mo = 5.00, V = 3.00,W = 6.30, Co = 8.40
    Supply Condition Annealed 300 HB Max
    Nearest Equivalent DIN 1.3244, ASSAB ASP30
  • Stainless Chromium Steel
    Chemical composition C = 0.9, Si = 0.45, Mn = 0.4, Cr = 1.75, Mo = 1.1, V = 0.1
    Supply Condition Annealed 265 HB
    Nearest Equivalent DIN 1.4112, AISI 440B, JIS SUS440B
    Chemical composition C = 1.05, Si = 0.4, Mn = 0.4, Cr = 17.0, Mo = 0.50
    Supply Condition Annealed 285 HB
    Nearest Equivalent DIN 1.4125, AISI 440C, JIS SUS440C
    Chemical composition C = 0.04, Si = 0.25, Mn = 0.40, Cr = 15.40, Ni = 4.40, Cu = 3.30,Nb = 0.30
    Supply Condition Solution Annealed 33-38 HRC
    Nearest Equivalent DIN 1.4542, AISI 630
  • Heat Treating Steel
    Chemical composition C = 0.34, Si = 0.3, Mn = 0.5, Cr = 1.5, Mo = 0.2, Ni = 1.5
    Supply Condition Prehardened 28-32 HRC (270-310 HB)
    Nearest Equivalent DIN 1.6582 35CrNiMo6, AISI 4340, JIS SNCM1
    Chemical composition C = 0.41, Si = 0.3, Mn = 0.7, Cr = 1.1, Mo = 0.2
    Supply Condition Prehardened 28-32 HRC (270-310 HB)
    Nearest Equivalent DIN 1.7225 42CrMo4, AISI 4140, JIS SCM440
  • Special Material/Aerospace & Automative
        Special Materials Energy / Oil, Gas & Chemical Processing Industry (CPI)
        Special Materials Energy / Power Generation
        Special Materials Energy / Engineering
     

 

Our Company

โทรศัพท์ : 66(0) 2295-1000-8,66(0) 2295-1901-6
แฟกซ์ : 66(0) 2295 1009 , 66(0) 2683 0943 , 66(0) 2683 0944
ที่อยู่ : 42, 48 ถนน พระราม 3, ซอย 53, ยานนาวา, กรุงเทพ 10120
โทรศัพท์ : 66(0) 38-080-400 , 66(0) 38-080-411
แฟกซ์ : 66(0) 38-080-409 , 66(0) 38-080-419 , 66(0) 38-080-429
ที่อยู่ : 155 หมู่ 14 ถนน สุขุมวิท, บางปะกง, ฉะเชิงเทรา 24130

Visit Us