- Tool Steel
- Cold Work Steel
Chemical composition C = 2.0, Si = 0.25, Mn = 0.30, Cr = 11.5 Supply Condition Annealed 250 HB Nearest Equivalent DIN 1.2080, AISI D3, JIS SKD1 Chemical composition C = 1.6, Cr = 11.5, Mo = 0.6, V = 0.3, W = 0.5 Supply Condition Annealed 250 HB Nearest Equivalent DIN 1.2601 , AISI D2, JIS SKD11 Chemical composition C = 2.1, Si = 0.25, Mn = 0.35, Cr = 11.5, W = 0.7 Supply Condition Annealed 250 HB Nearest Equivalent DIN 1.2436, AISI D6 Chemical composition C = 1.55, Si = 0.25, Mn = 0.35, Cr = 11.8, Mo = 0.8, V = 0.95 Supply Condition Annealed 235 - 250 HB Nearest Equivalent DIN 1.2379, AISI D2, JIS SKD 11 Chemical composition C = 1.10, Si = 0.90, Mn = 0.40, Cr = 8.30, Mo = 2.10,V = 0.50,+ Al, Nb Supply Condition Annealed 250 HB Chemical composition C = 0.82, Si = 0.70, Mn = 0.40, Cr = 8.00, Mo = 1.60, V = 0.60+ Al = + Supply Condition Annealed 240 HB Max. Chemical composition C = 2.47, Si = 0.55, Mn = 0.40, Cr = 4.20, Mo = 3.8, V = 9.00,W = 1.00, Co = 2.00 Supply Condition Annealed 280 HB Max. Chemical composition C = 1.40, Cr = 6.40, Mo = 1.50, V = 3.70, W = 350, Nb = + Supply Condition Annealed 280 HB Max. Chemical composition C = 0.95, Si = 0.25, Mn = 1.10, Cr = 0.55, V = 0.10, W = 0.55 Supply Condition Annealed 225 HB Nearest Equivalent DIN 1.2510, AISI O1, JIS SKS21 (SKS3) Chemical composition C = 1.18, Si = 0.25, Mn = 0.30, Cr = 0.70, V = 0.10 Supply Condition Annealed 220 HB Nearest Equivalent DIN 1.2210, 115CrV3 - Hot Work Steel
Chemical composition C = 0.39, Cr = 5.2, Mo = 1.4, V = 0.95, Si = 1.1, Mn = 0.40 Supply Condition Annealed 230 – 235 HB Nearest Equivalent DIN 1.2344, AISI H13, JIS SKD61 Chemical composition C = 0.38, Si = 0.4, Mn = 0.4, Cr = 5.0, Mo = 2.8, V = 0.65 Supply Condition Annealed 230 – 235 HB Nearest Equivalent DIN 1.2367 Chemical composition C = 0.39, Cr = 2.9, Mn = 0.35, Mo = 2.8, V = 0.65, Si = 0.3,Co = 2.9 Supply Condition Annealed 230 - 235 HB Nearest Equivalent DIN 1.2885, ~X32CrMoCoV3-3-3 Chemical composition C = 0.50, Cr = 4.50, Mo = 3.00, V = 0.55, Si = 0.20, Mn = 0.25 Supply Condition Annealed max 205 HB Chemical composition C = 0.38, Cr = 5.00, Mo = 2.80, V = 0.65, Si = 0.20, Mn = 0.25 Supply Condition Annealed max 205 HB Nearest Equivalent DIN ~1.2367 Chemical composition C = 0.55, Si = 0.25, Mn = 0.75, Cr = 1.1, Mo = 0.50, Ni = 1.7,V = 0.10 Supply Condition Prehardened 38-42 HRC Nearest Equivalent DIN 1.2714, AISI L6, JIS SKT4 - Plastic Mould Steel
Chemical composition C = 0.40, Si = 0.3, Mn = 1.5, Cr = 2.0, Mo = 0.2, S = 0.02,Ni = 1.0 Supply Condition Prehardened 28–32 HRC (280–325 HB), High Hard 38–42 HRC Nearest Equivalent DIN 1.2738, ASSAB 718 Chemical composition C = 0.35-0.45, Si = 0.20-0.40, Mn = 1.30-1.60, Cr = 1.80-2.10,Mo = 0.15-0.25, S = 0.002 max Supply Condition Prehardened 28-32 HRC (280-325 HB) Nearest Equivalent AISI P20, DIN 1.2311 Chemical composition C = 0.40, Si = 0.40, Mn = 1.50, Cr = 1.90, Mo = 0.20, S = 0.07 Supply Condition Prehardened 28-32 HRC (280-325 HB) Nearest Equivalent DIN 1.2312, AISI P20 Chemical composition C = 0.38, Si = 0.30, Mn = 1.50, Cr = 2.00, Mo = 0.20, Ni = 1.10 Supply Condition Harden and tempered 38-42 HRC (350-400 HB), High Hard Nearest Equivalent DIN 1.2738 Chemical composition C = 0.38, Si = 0.4, Cr = 16.0, Mo = 1.0, Ni = 0.8, Mn = 0.65 Supply Condition Prehardened 28-32 HRC Nearest Equivalent DIN 1.2316, ~X36CrMo17 Chemical composition C = 0.27, Cr = 14.7, Mo = 1.00, Ni = 0.80, Si = 0.30, Mn = 0.55,+ N Supply Condition Prehardened 28-32 HRC, High Hard 38-42 HRC Nearest Equivalent DIN ~1.2316 Chemical composition C = 0.41, Si = 0.70, Mn = 0.45, Cr = 14.30,Mo = 0.60, V = 0.20 Supply Condition Annealed 200 HB Nearest Equivalent DIN 1.2083, AISI 420, JIS SUS 420J2, ASSAB STAVAX Chemical composition C = 0.05, Si = 0.20, Mn = 0.90, S = 0.12, Cr = 12.80, Ni = + Supply Condition Prehardened 28-32 HRC (280-320 HB) Chemical composition C = 0.28, Si = 0.3, Mn = 0.3, Cr = 13.5, +N Supply Condition Annealed 220 HB Chemical composition C = 0.54, Si = 0.45, Mn = 0.40, Cr = 17.30, Mo = 1.10, V = 0.10,+ N Supply Condition Annealed 260 HB Chemical composition C = 0.13, Si = 0.30, Mn = 2.00, Cr = 0.35, Ni = 3.50, Cu = 1.20,Al = 1.20 Supply Condition Hardened 38-42 HRC Nearest Equivalent AISI ~P21, DAIDO NAK80 - Powder Metallurgical
S790 PMS290 PMS390 PMS590 PM
- Cold Work Steel
- High Speed Steel
Chemical composition C = 0.90, Cr = 4.1, Mo = 5.0, V = 1.8, W = 6.2 Supply Condition Annealed 280 HB Max. Nearest Equivalent DIN 1.3343, AISI M2, JIS SKH51 Chemical composition C = 0.92, Si = 0.4, Mn = 0.3, Cr = 4.1, Mo = 5.0, V = 1.9,W = 6.4, Co = 4.8 Supply Condition Annealed 270-300 HB Nearest Equivalent DIN 1.3243, AISI M41, JIS SKH55 Chemical composition C = 1.30, Si = 0.60, Mn 0.30, Cr = 4.20, Mo = 5.00, V = 3.00,W = 6.30 Supply Condition Annealed 280 HBx Nearest Equivalent DIN 1.3345, ASSAB ASP23 Chemical composition C = 2.00, Si = 0.5, Mn = 0.3, Cr = 3.8, Mo = 2.5, V = 5.1,W = 14.3, Co = 11.0 Supply Condition Annealed 350 HB Max Chemical composition C = 1.64, Si = 0.60, Mn = 0.30, Cr = 4.80, Mo = 2.00,V = 4.80, W = 10.40, Co = 8.00 Supply Condition Annealed 300 HB Max Nearest Equivalent ASSAB ASP60 Chemical composition C = 1.1, Si = 0.5, Mn = 0.2, Cr = 3.9, Mo = 9.2, V = 1.0,W = 1.4, Co = 7.8 Supply Condition Annealed 280 HB Max Nearest Equivalent DIN 1.3247, AISI M42, JIS ~SKH59 Chemical composition C = 1.29, Si = 0.60, Mn = 0.30, Cr = 4.20, Mo = 5.00, V = 3.00,W = 6.30, Co = 8.40 Supply Condition Annealed 300 HB Max Nearest Equivalent DIN 1.3244, ASSAB ASP30 - Stainless Chromium Steel
Chemical composition C = 0.9, Si = 0.45, Mn = 0.4, Cr = 1.75, Mo = 1.1, V = 0.1 Supply Condition Annealed 265 HB Nearest Equivalent DIN 1.4112, AISI 440B, JIS SUS440B Chemical composition C = 1.05, Si = 0.4, Mn = 0.4, Cr = 17.0, Mo = 0.50 Supply Condition Annealed 285 HB Nearest Equivalent DIN 1.4125, AISI 440C, JIS SUS440C Chemical composition C = 0.04, Si = 0.25, Mn = 0.40, Cr = 15.40, Ni = 4.40, Cu = 3.30,Nb = 0.30 Supply Condition Solution Annealed 33-38 HRC Nearest Equivalent DIN 1.4542, AISI 630 - Heat Treating Steel
Chemical composition C = 0.34, Si = 0.3, Mn = 0.5, Cr = 1.5, Mo = 0.2, Ni = 1.5 Supply Condition Prehardened 28-32 HRC (270-310 HB) Nearest Equivalent DIN 1.6582 35CrNiMo6, AISI 4340, JIS SNCM1 Chemical composition C = 0.41, Si = 0.3, Mn = 0.7, Cr = 1.1, Mo = 0.2 Supply Condition Prehardened 28-32 HRC (270-310 HB) Nearest Equivalent DIN 1.7225 42CrMo4, AISI 4140, JIS SCM440 - Special Material/Aerospace & Automative
Special Materials Energy / Oil, Gas & Chemical Processing Industry (CPI)Special Materials Energy / Power GenerationSpecial Materials Energy / Engineering
- Knife Steels
Knife Steel: K294, N360, N540,N680, N685, N690, N695, M368, M390, M398
Tailor-made sheets/ plates for:
- Cutter knives / knives for meat and sausage processing
- Knives for industrial fish processing
- High-quality application, e.g. hunting knives and kitchen knives
- Knives for the cardboard and paper industry
- Knives for textile industry
- Knives for metal and plastic processing